Volkswagen Golf Service & Repair Manual: Wax-based underseal -D 316 000 A1

Designation:
Wax-based underseal -D 316 000 A1-
Issued 01.2008
Product description
Wax underseal -D 316 000 A1- offers excellent long-term underbody corrosion protection.
Wax underseal is based on a solvent-free, oxidative-drying system and offers excellent underbody corrosion protection.
This corrosion protection is the result of very good adhesion to metal surfaces at both very low and high temperatures.
The product creates a light-brown, elastic coating which is firm to the touch.
It is not necessary to raise the temperature to produce a film coating.
Technical data sheet, wax underseal -D 316 000 A1-
Application
The material is used primarily in automotive applications.
Ensure that the substrates are dry.
The ready-to-use product is applied by brush at a material temperature between 20 and 35 °C.
When required by the application method, the material can be gently heated to maximum 45 °C directly () before application.
The oxidative curing product may already develop a skin on the surface after only a short time. This has no influence on its anti-corrosion protection or other properties
Properties
Solvent-free
Active ingredient content: 100%
Excellent long-term anti-corrosion protection
Good adhesion
Low tendency to drip
Low-temperature flexibility
Long storage life
  Note
Before using, read the safety measures and recommendations in the safety data sheet.
Even for products which are not required by law to be labelled, the usual safety measures for chemical products must be observed.
Application
The surfaces to be treated must be dry and free of grease or dust.
Bring wax-based underseal to application temperature (20-35 °C).
Apply material to body parts which are to be protected and spread with a brush.
Technical data
   
Base Mixture of anti-corrosion additives on sulfonate basis, alkyd resin, special mineral oil raffinates, pigments, thickeners, drying accelerators and fluorescent pigments.
Form and colour as supplied light-brown, viscous liquid
Rheomat viscosity 1850 ± 350 mPas (PP50 system, d= 760 1/s)
Density at 15 °C DIN EN ISO 12185 0.995 ± 0.015 g/ml
Solids content 99 ± 1 %
Flashpoint DIN EN ISO 2719 Approx. 150 °C
Recommended coat thicknesses 100-400 µm
Working temperature +20 °C to +35 °C
Storage Approx. 12 months at temperatures between +10 °C and 30 °C
Container 310 ml
Wax-based underseal -D 316 D38 A2
Designation: Wax-based underseal -D 316 D38 A2- Issued 04.2009 Product description ...

Spray wax (spraying wax) -D 322 100 M2
Designation: Spray wax (spraying wax) -D 322 100 M2- Issued 01.2011 Product description ...

Other materials:

Removing and installing steering rack, RHD vehicles, except for e-Golf
Special tools and workshop equipment required Ball joint puller -T10187- Torque wrench -V.A.G 1331- Torque wrench -V.A.G 1332- Engine and gearbox jack -V.A.G 1383 A-   Removing ...

Assembly overview - skid plate
  Note The removal and installation procedures may have to be modified slightly depending on engine fitted. 1 -  Underride guard Removing –  Remove bolts -2-, -3- and -4-. –  Pull out noise ...

Repairs to wiring with cross sections up to 0.35 mm2
Special tools and workshop equipment required Crimping pliers, complete -VAS 1978/1 A-     Head adapter 0.35 mmІ - 2.5 mmІ -VAS 1978/1-1- For repairs to ...

© 2016-2020 Copyright www.vwgolf.org