Volkswagen Golf Service & Repair Manual: 2-pack HS Performance clear coat
| 2-pack HS Performance clear coat -LZK 769 K06 A5- |
| 2-pack HS Performance clear coat is a high-gloss, VOC
compliant, high-solid clear coat. |
| Flexible application in all areas of repair |
| Flexible application in one-and-a-half spray coats
(preferred) or two coats (possible) |
| Good gloss and filling power |
|
|
|
| 2-pack VHS hardener -LHA 009 051 A2-/-LVM 009 051 A5- |
| 2-pack VHS hardener, fast-drying -LHA 009 050 A2- |
| 2-pack VHS hardener, slow-drying -LHA 009 052 A2-/-LHA 009
052 A3- |
| 2-pack VHS hardener, extra slow-drying -LHA 009 053 A2- |
| The choice of hardener depends on the temperature and size
of the surface. See technical data sheet for 2-pack VHS hardener
→ Chapter. |
| For elasticization, see
→ Anchor |
| Clear coat additive -LVM 007 000 A2- |
| HS spot thinner -LVM 006 000 A2- |
| See technical data sheet for 2-pack HS spot thinner
→ Chapter |
|
|
|
| Application time/pot life: |
| – |
Mixed for spraying, 60 to 120 minutes at +20°C |
|
|
|
| Method of application: “spray”. |
|
|
|
| – |
Application viscosity 4 mm, +20 °C, DIN 53211 |
| Application viscosity 4 mm, gravity-feed spray gun
“compliant” and “HVLP”. |
|
|
|
| Add 5% clear coat additive -LVM 007 000 A2- at a material
temperature of +20 °C |
 Note
| When used as clear coat for spot repairs (Clever Repair
method), the 5% clear coat additive -LVM 007 000 A2- may be
replaced with 5% HS spot thinner -LVM 006 000 A2-. |
| The mixture described here for the Clever Repair method must
not be used on horizontal surfaces. |
| – |
If thinner is added, use measuring stick to mix. |
|
|
|
| – |
Adjust spray nozzle following manufacturer's instructions to
1.3-1.4 mm for “compliancy”. |
| – |
Adjust spray nozzle following manufacturer's instructions to
1.3-1.4 mm for “HVLP”. |
| – |
Adjust spray pressure following manufacturer's instructions
to 2.0-2.5 bar for “compliancy”. |
| – |
Adjust atomising pressure following manufacturer's
instructions to 0.7 bar for “HVLP”. |
|
|
|
| Can be applied in one-and-a-half coats; that is, the first
half coat forms a thin, nearly uniform film, upon which a
complete, uniform coat is sprayed. |
| Apply in two spray coats with 5-10 minutes intermediate
flash-off time The first coat is applied with restraint, but
still uniformly. |
| – |
The specified thickness for the dry film is 50-70 µm. |
|
|
|
| Air drying at +18 to 22 °C ambient temperature: |
|
|
|
| Final flash-off time with force drying is at least
5-10 minutes. |
|
|
|
| Force drying at +60-65 °C material temperature in
25-35 minutes. |
|
|
|
| Final flash-off time with infrared drying is at least
5-10 minutes. |
|
|
|
| Infrared drying with short-wave radiant heater,
10-15 minutes |
|
|
|
| Elasticization of rigid and semi-rigid plastics: |
| First mix the base material with 15% elastic additive -ALZ
011 001-. |
| Mixture with 2-pack VHS hardeners, 3:1 with 5% clear coat
additive -LVM 007 000 A2- (drying time increases). |
|
|
|
| Personal protective equipment: |
| Adhere to the safety data sheet. |
| Wear personal protective equipment during application. |
|
|
|
| Flash point: |
Above +23 °C |
| VOC content:
2004/42/IIB(d)(420)420 |
The EU limit value for this
product (product category IIB.b) in ready-to-spray form is max. 420 g/l
of volatile organic compounds. The VOC content of this product in
ready-to-spray form is max. 420 g/l. |
| 2-pack HS Brillant plus clear coat -LZK 769 K05 A5-, 48
months from production date. |
| Clear coat additive -LVM 007 000 A2- 24 months from
production date. |
| May be used until the date stated on the label at latest if
stored in sealed original containers at +20 °C. |
|
|
|
Designation:
2-pack HS Brillant plus clear coat -LZK 769 K05 A5-
Issued 02.2012
Product description
...
Designation:
Blender -LVE 013 100 A2-
Issued 10.2012
Product description
Blender ...
© 2016-2024 Copyright www.vwgolf.org
2-pack HS Brillant plus clear coat
Blender